Nano cerium oxide pauta CeO2 nanopowder/nanoparticles
Fa'amatalaga pupuu
1. Igoa: Cerium Dioxide;Ceric oxide;Cerium oxide;
2. fua mole: CeO2
3. Mama: 99.9% 99.99% 99.999% faitalia
4. Lanu: tele nano, 30-50nm, 50-100nm (paʻu samasama malamalama),
micron lapoa, 1-10um, (e masani ona pa'epa'e pa'epa'e)
5.Numera CAS: 1306-38-3
Fa'amatalaga autu
Cerium oxide o se ituaiga mea inorganic, fua fa'ama'i CeO2, lanu samasama po'o samasama enaena pauta.Density 7.13g/cm3, liusuavai 2397 ℃, le mafai ona solu i le vai ma alkali, soluble teisi i le acid.
I lalo o le vevela o le 2000 ℃ ma le mamafa o le 15MPa, e mafai ona maua le ceria e ala i le faʻaitiitia o le ceria ma le hydrogen.Pe a maua fua le vevela ile 2000 ℃ ma le mamafa e leai se totogi ile 5MPa,
Cerium oxide e samasama mumu, ma piniki, o lona faatinoga o le faia o mea polesi, catalyst, catalyst carrier (fesoasoani), absorber ultraviolet, suauu suauu electrolyte,Su'e afi ta'avale, sima eletise, ma isi.
natura:
1. E le faigofie ona fausia pores pe a faʻaopopo le cerium oxide nano-sized i ceramics, lea e mafai ona faʻaleleia atili ai le mamafa ma le maeʻa o ceramics.
2, nano cerium oxide o loʻo i ai se gaioiga faʻamalosi lelei, talafeagai mo le faʻaogaina i mea faʻapipiʻi poʻo catalysts;
3, nano cerium oxide e mafai ona faʻaaogaina mo palasitika, paʻu anti-ultraviolet, anti-matua, faʻamauina vevela vevela, ma isi.
Talosaga fanua:
1, Catalyst, polesi, vailaʻau faʻapipiʻi, mea faʻaeletoroni, mea faʻapipiʻi, faʻapipiʻi UV, mea maa.
2. Omea lelei aoga;Faʻaopoopo i ceramics e mafai ona faʻaitiitia ai le vevela o le sintering, faʻalavelave le tuputupu aʻe o lattice, faʻaleleia le mamafa o keramika;
3, Alloy coating: faʻaopoopo le zinc nickel, zinc drill ma le zinc uʻamea uʻamea e sui ai le electrocrystallization faagasologa o le zinc, faʻaleleia le tioata tioata e maua ai le faʻatonuga sili, faʻapipiʻi microstructure e sili atu le toniga, sili atu le mafiafia, ma faʻaleleia atili ai le faʻafefeteina o le ufiufi;
4, Polymer: e mafai ona faʻateleina le faʻamautuina o le vevela o le polymer ma le matua tetee.
5, Faʻaaogaina e pei o le palasitika, faʻamautu vevela paʻu ma sui faʻamaʻi matua
6, I le avea ai o se lubricant palasitika, faʻaleleia le faʻaogaina o le palasitika o palasitika,
7, Mo le faaiila.
Fa'amatalaga
Oloa Igoa | Cerium Oxide | |||
CeO2/TREO (% min.) | 99.999 | 99.99 | 99.9 | 99 |
TREO (% min.) | 99 | 99 | 99 | 99 |
Ma'imau ile mu (% max.) | 1 | 1 | 1 | 1 |
Fa'alelalolagi seāseā | ppm maualuga. | ppm maualuga. | % maualuga. | % maualuga. |
La2O3/TREO | 2 | 50 | 0.1 | 0.5 |
Pr6O11/TREO | 2 | 50 | 0.1 | 0.5 |
Nd2O3/TREO | 2 | 20 | 0.05 | 0.2 |
Sm2O3/TREO | 2 | 10 | 0.01 | 0.05 |
Y2O3/TREO | 2 | 10 | 0.01 | 0.05 |
Fa'alelalolagi e le'o seasea maua | ppm maualuga. | ppm maualuga. | % maualuga. | % maualuga. |
Fe2O3 | 10 | 20 | 0.02 | 0.03 |
SiO2 | 50 | 100 | 0.03 | 0.05 |
CaO | 30 | 100 | 0.05 | 0.05 |
PbO | 5 | 10 | ||
Al2O3 | 10 | |||
NiO | 5 | |||
CuO | 5 |